Heat treatment processes for alloys
| Materials | Marking | Heat treatment processes |
|---|---|---|
| Ni3Al-Ni3V | Rise to 1 175 ℃ from room temperature and hold 0.5 h, continue to rise to 1 205 ℃ holding 2.5 h, and cool to room temperature. The heating rate is (20±3) ℃/min | |
| Ni3Al-Ni3V-Zr-Ni5Zr | Sample 1 | Rise to 1 175 ℃ from room temperature and hold 0.5 h, continue to rise to 1 205 ℃ holding 2.5 h, and cool to room temperature. The heating rate is (20±3) ℃/min |
| Sample 2 | Rise to 1 175 ℃ from room temperature and hold 0.5 h, continue to rise to 1 205 ℃ holding 2.5 h, cool to room temperature, then rise to 1 100 ℃ holding 10 h, and cool to 1 000 ℃ holding 10 h. The heating rate is (20±3) ℃/min | |
| Sample 3 | Rise to 1 175 ℃ from room temperature and hold 0.5 h, continue to rise to 1 205 ℃ holding 2.5 h, cool to room temperature, reheat to 1 175 ℃ holding 2.5 h, then cool to 1 080 ℃ holding 4.5 h. The heating rate is (20±3) ℃/min |
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.